t_skema.gif (12113 bytes)  Measurements and Sizes

Description Size Thickness of Material Composition of Material
SS33 Bolt Diam 32.25 mm - 33.75 mm Nominal 2.3 mm ASTM A607 Grade 60 Class 1
SS39 Bolt Diam 37.50 mm - 39.0 mm Nominal 2.3 mm ASTM A607 Grade 60 Class 1
SS46 Bolt Diam 44.50 mm - 26.0 mm Nominal 3.2 mm ASTM A607 Grade 60 Class 1
SS125 Plate 125 mm  x  125 mm (2 mm) Nominal 4.5 mm SABS 1431 Grade 300 WA
SS150 Plate 150 mm  x  150 mm (2 mm) Nominal 6.0 mm SABS 1431 Grade 300 WA

For 39mm bolts begin with drill bits smaller than 1.375" (35mm) Diameter

For 33mm bolts begin with drill bits smaller than 1.275" (32mm) Diameter

Pull test bolts - Optimum bit size will vary with ground conditions

t_skema.gif (12113 bytes)  Weights

Description Standard Iron Hot Dipped Galvanized
  SS33B SS39B SS46B SS33G SS39G SS46G
Bolt 18 inches long 0.74 kg 0.86 kg 1.34 kg 0.81 kg 0.95 kg 1.47 kg
Bolt 2 feet long 0.96 kg 1.12 kg 1.76 kg 1.06 kg 1.23 kg 1.94 kg
Bolt 3 feet long 1.42 kg 1.66 kg 2.61 kg 1.56 kg 1.83 kg 2.87 kg
Bolt 4 feet long 1.88 kg 2.19 kg 3.46 kg 2.07 kg 2.41 kg 3.81 kg
Bolt 5 feet long 2.34 kg 2.72 kg 4.30 kg 2.57 kg 2.99 kg 4.73 kg
Bolt 5 feet 9 inches long 2.68 kg 3.13 kg 4.94 kg 2.95 kg 3.44 kg 5.43 kg
Bolt 6 feet long 2.79 kg 3.26 kg 5.15 kg 3.07 kg 3.59 kg 5.67 kg
Bolt 7 feet long 3.25 kg 3.79 kg 6.00 kg 3.58 kg 4.17 kg 6.60 kg
Bolt 8 feet long 3.71 kg 4.33 kg 6.85 kg 4.08 kg 4.76 kg 7.54 kg
Plate 125 mm x 125 mm 0.50kg 0.55kg
Plate 150 mm x 150 mm 0.70kg 0.77kg

Please note: hot dip galvanizing adds 10% to the weight of the product.

Send mail to webmaster@partshq.com with questions or comments about this web site or travel to Reach Us.

Copyright 1997 Parts HeadQuarters Inc. All rights reserved. Information in this document is subject to change without notice.
Other products and companies referred to herein are trademarks or registered trademarks of their respective companies or mark holders.


Last modified: March 14, 2017